Improvement in CO2 Capture of Polyamine with Micro-Interfacial System.

Polyamines have emerged as a promising class of CO2 absorbents due to their remarkable sequestration capacity. However, their potential industrial application as aqueous absorbents is significantly hindered by a low regeneration efficiency and high energy consumption. To address these issues, this study investigates the use of triethylenetetramine (TETA) and ethylene glycol (EG) to develop a nonaqueous absorbent. The incorporation of EG enhances absorption performance and reduces the regeneration energy needed for TETA, whereas the high viscosity of the absorbent impedes absorption rate, amine efficiency, and regeneration efficiency. In order to enhance CO2 capture, micron-sized reaction units (SiO2@TETA-EG) were developed by encapsulating TETA solution with nanosilica. The SiO2@TETA-EG composite exhibits a large specific surface area (99 m2/g), with a porous shell structure and improved fluidity, which effectively counteracts the negative effects caused by high viscosity. Notably, SiO2@TETA-EG indicates a noticeably higher apparent rate constant of 4.29 min-1 at 323.2 K compared to the TETA-EG solution. Furthermore, SiO2@TETA-EG displays a 28.4% boost in regeneration efficiency while maintaining favorable stability in pore size and shape after regeneration.

Degradation Characteristics of Cellulose Acetate in Different Aqueous Conditions.

Cellulose acetate (CA) is widely used in cigarette filters and packaging films, but due to its acetylation, it is difficult to degrade in the natural environment, and the problem of pollution has become a serious challenge. Understanding the degradation behavior and performance of CA in different environments is the basis and prerequisite for achieving its comprehensive utilization and developing efficient degradation methods. In this study, we investigated the degradation performance of CA in different aqueous environments to evaluate the effects of pH, salinity and microorganisms on CA degradation. The CA tows and films were immersed in HCl, NaOH solution, river water, seawater or homemade seawater for 16 weeks and the degradation mechanism was investigated by the changes in weight loss rate, degree of substitution, hydrophilicity, molecular structure and surface morphology. The results showed that the degradation of CA tow and film were the fastest in NaOH solution; the weight loss rates after 16 weeks were 40.29% and 39.63%, respectively, followed by HCl solution, and the degradation performance of CA tow was better than that of film. After 16 weeks of degradation in river water, seawater and homemade seawater, all the weight loss rates were less than 3%. In summary, this study illustrated that the environmental acidity, basicity and high concentration of inorganic salts had a critical promotion effect on the non-enzymatic hydrolysis of CA, whereas the number and type of microorganisms were the key factors affecting the biodegradation of CA.